项目(Item) |
试验方法 Test ASTM |
单位 Unit |
条件 Test condition |
PBT 6100 Gxx (普通阻燃增强) |
PBT 6200 Gxx (环保增强阻燃) | ||||||||||
G0 |
G10 |
G15 |
G20 |
G25 |
G30 |
G0 |
G10 |
G15 |
G20 |
G25 |
G30 | ||||
密度(Density) |
D792 |
g/cm2 |
23℃ |
1.4 |
1.45 |
1.52 |
1.54 |
1.58 |
1.61 |
1.4 |
1.45 |
1.5 |
1.54 |
1.58 |
1.6 |
成型收缩率(Shrinkageration) |
D570 |
% |
0.1 |
0.08 |
0.07 |
0.05 |
0.05 |
0.05 |
0.1 |
0.08 |
0.07 |
0.05 |
0.05 |
0.05 | |
拉伸强度(Tensile strength) |
D638 |
mpa |
55 |
85 |
95 |
100 |
110 |
115 |
55 |
85 |
95 |
100 |
110 |
115 | |
拉伸模量(Tensile modulus) |
D638 |
mpa |
|||||||||||||
弯曲强度(Flexural strength) |
D790 |
mpa |
75 |
125 |
135 |
145 |
165 |
175 |
75 |
125 |
135 |
145 |
165 |
175 | |
弯曲模量(Flexural modulus) |
D790 |
mpa |
4500 |
6000 |
6500 |
7000 |
8000 |
8500 |
4500 |
6000 |
6500 |
7000 |
8000 |
8500 | |
缺口(Unnotched) |
D256 |
kj/m2 |
4 |
5 |
6 |
7 |
8 |
9 |
4 |
5 |
6 |
7 |
8 |
9 | |
无缺口(Notched) |
D256 |
kj/m2 |
50 |
40 |
45 |
50 |
55 |
60 |
50 |
40 |
45 |
50 |
55 |
60 | |
热变形温度(HDT) |
D648 |
℃ |
0.46mpa |
180 |
200 |
205 |
210 |
215 |
220 |
180 |
200 |
205 |
210 |
215 |
220 |
1.82mpa |
70 |
190 |
195 |
200 |
205 |
207 |
70 |
190 |
195 |
200 |
205 |
207 | |||
燃烧性(Flammability) |
UL94 |
0.8--1.6mm |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 |
v0 | |
介电常数(Dielectric constant) |
D150 |
50Hz |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 | |
介电损耗角正切(Dielectric losstangent) |
D150 |
50Hz |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 | |
体积电阻率(Volume resistivety) |
D257 |
Ω.cm*1016 |
2mm厚 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
介电强度(Molding condition) |
D149 |
MV/m |
2mm厚 |
19 |
19 |
20 |
20 |
20 |
20 |
19 |
19 |
20 |
20 |
20 |
20 |
*以上数据为典型数据,并非产品出厂标准,仅供用户选型时参考 |
The date do not mean product standard ,they are given to custcmers for reference while selecting and purchasing |